Marca: H-Tong
Standard: Aisi, Astm, Din, Gb
Place Of Origin: China
Species: Steel Plate
Production Process: Hot Rolled
Application: Boiler Plate, Container Plate, Ship Plate
Special Steel: Wear Resistant Steel, High-Strength Steel Plate
Tolerance: ±1%, ±3%
Category: Cold Rolled Steel Sheet, Boiler Vessel Plate, Low-Alloy Plate, Hot Rolled Steel Sheet, Steel Plate, Ship Steel Plate
Processing Service: Welding, Cutting, Decoiling, Punching, Bending
Surface Treatment: Coated, Clean, blasting and painting according to customer requirement
Thickness: 3-120mm
Width: 600-1500mm, 1800-2000mm,2500-3500mm
Length: 2000-3000mm, 6000-12000mm
Unidades de venta | : | Ton |
Tipo de paquete | : | paquete con tira de acero |
Ejemplo de una imagen | : |
Plato de ropa de superposición de carburo de cromo se fabrican soldando una o múltiples capas resistentes a desgaste en una placa base de acero mediano o bajo en carbono.
La aleación de superposición tiene una gran cantidad de partículas duras de carburo de cromo que hace que la placa tenga un buen desgaste y resistencia al impacto.
Rango de espesor de superposición : 3-25 mm
Tamaño de la placa de desgaste: 1500*3000, 1400*3000,1400*3400, 1400*3500, 2100*3500, personalizado.
La placa de acero de la superposición de carburo de cromo se usa para hacer que muchas piezas de desgaste complejas se coloquen en lugares de alto desgaste.
Podemos proporcionar un corte de placas de desgaste, doblar, atornillar, golpear y soldar de acuerdo con los dibujos del cliente.
1. La placa de acero resistente a la ropa está compuesta por una placa de acero baja en carbono y una capa resistente al desgaste de aleación. Cuando se trabaja, la matriz proporciona propiedades integrales, como resistencia, resistencia y plasticidad de resistir fuerzas externas, y la capa de aleación resistente al desgaste proporciona propiedades resistentes al desgaste que cumplen con los requisitos de las condiciones de trabajo específicas.
2. La capa y la placa base de aleación de acero resistente a la ropa de ropa son una combinación metalúrgica. Mediante el equipo especial y el proceso de soldadura automática, el cable de aleación autoprotectante de alta duración está soldado uniformemente en el sustrato, y las capas compuestas son de una a dos o incluso más. En el proceso compuesto, debido a la diferente relación de contracción de la aleación, aparecen grietas transversales uniformes, que es una característica significativa de la placa de acero resistente al desgaste.
3. La capa resistente al desgaste de la aleación es principalmente aleación de cromo, mientras que se agregan manganeso, molibdeno, niobio, níquel y otras aleaciones. La microdureza del carburo puede alcanzar por encima de HV1700-2000, y la dureza de la superficie puede alcanzar HRC58-62. La aleación de carburo tiene una fuerte estabilidad a alta temperatura, mantiene una alta dureza, pero también tiene una buena resistencia a la oxidación, dentro de 500 ℃ Uso completamente normal.
4. La capa resistente al desgaste tiene canal estrecho (2.5-3.5 mm), canal ancho (8-12 mm), curva (S, W), etc. Se compone principalmente de aleación de cromo, mientras que manganeso, molibdeno, niobio, níquel , se agregan Boron y otros componentes de aleación. Con un contenido de carburo del 40-60%, la microdureza puede alcanzar HV1700 y la dureza de la superficie puede alcanzar HRC58-62.
Product |
Wear Resistant Steel Plate |
Standard |
AISI,ASTM,DIN,JIS,GB,JIS,SUS,EN,etc. |
Thickness |
3-120mm |
Width |
600-1500mm, 1800-2000mm,2500-3500mm |
Length |
2000-3000mm, 6000-12000mm |
Grade |
NM360, NM400, NM450, NM500, AR360, AR400, AR450, AR500, AR550
QUARD400, QUARD450, QUARD500, FORA400, FORA500, RAEX400, RAEX450, RAEX500 |
Surface treatment |
Clean, blasting and painting according to customer requirement |
Technique |
Cold rolled and hot rolled |
Capacity |
10000 tons/month |
Package |
Export standard packing: wooden cases or boxes to be packed;We will pack the goods according to the factory's requirements for export. Or according to customer requirements.In addition,we will give the product good surface protection. |
Application |
metallurgy, coal, cement, power stntion, mining, building materials, petrochemical industry |
NM360 NM 400 NM 450 NM 500 Placa de acero de resistencia al desgaste
Componente químico
Steel/Grade |
C |
Si |
Mn |
P |
S |
AL |
Cr+Ni+Mo |
Nb+V+Ti |
NM360/AR360 |
0.10-0.30 |
0.20-0.40 |
1.00-2.00 |
≤0.015 |
≤0.003 |
≥0.20 |
<0.6 |
Trace Amount |
NM400/AR400 |
0.10-0.40 |
0.20-0.40 |
1.00-2.00 |
≤0.015 |
≤0.003 |
≥0.20 |
<0.9 |
|
NM450/AR450 |
0.10-0.40 |
0.20-0.40 |
1.00-2.00 |
≤0.015 |
≤0.003 |
≥0.20 |
<1.2 |
|
NM500/AR500 |
0.10-0.40 |
0.20-0.45 |
1.00-2.00 |
≤0.015 |
≤0.003 |
≥0.20 |
<1.5 |
|
NM550/AR550 |
0.10-0.50 |
0.20-0.45 |
1.00-1.50 |
≤0.015 |
≤0.003 |
≥0.20 |
<2.0 |
|
NM600/AR600 |
0.10-0.50 |
0.20-0.45 |
1.00-1.50 |
≤0.015 |
≤0.003 |
≥0.20 |
<2.5 |
Propiedades mecánicas
Material |
Tensile MPA |
Elongation% |
Impact energy -20℃ |
HBW |
NM300 |
≥1000 |
≥14 |
≥24 |
270-300 |
NM360 |
≥1100 |
≥12 |
≥24 |
330-390 |
NM400 |
≥1200 |
≥10 |
≥24 |
370-430 |
NM450 |
≥1250 |
≥7 |
≥24 |
420-480 |
NM500 |
≥1250 |
≥7 |
≥24 |
≥470 |
NM550 |
≥1250 |
≥7 |
≥24 |
≥530 |
NM600 |
≥1250 |
≥7 |
≥24 |
≥570 |
MN13 Placa de acero al carbono de alto manganeso
Composición química (%)
Material |
C |
Si |
Mn |
P |
S |
Mn13 |
0.90-1.20 |
0.30-0.80 |
11.0-14.0 |
≤0.035 |
≤0.30 |
Propiedades mecánicas
Tensile Strength |
Yield Point |
Elongation |
Impact Resistance |
Initial Hardness (HB) |
Hardness after Hardened (HB) |
180° old Bending Test |
≥900MPa |
≥295 |
≥40% |
ak≥90J |
200-250 |
≥300 |
Qualified |
Podemos producir diferentes tamaños, espesores, anchos y materiales de acuerdo con sus requisitos
1) Técnica de fabricación
Cortar placas de acero grandes como sus requisitos para hacer que la superficie de la placa brille por la lanza y la molienda, también puede hacer agujeros y hacer grados de ángulo, y puede soldar por su dibujo.
Para el grosor de menos de 30 mm, cortando por láser; Para un grosor de más de 30 mm, principalmente oxi cortado, corte de llama.
Para el grosor de la placa de acero de 200 mm, porque durante el corte de llama, la temperatura es muy alta, por lo que la placa de acero de las partes de corte puede romperse en la parte del ángulo, entonces nuestros trabajadores repararán los ángulos para que estén bien.
2 ) Aplicación
La placa de acero resistente al desgaste con alta resistencia al desgaste y un buen rendimiento de impacto es bueno, puede ser corte, flexión, soldadura, etc., puede adoptar la forma de soldadura, soldadura de enchufe, conexión de conexión de pernos para conectarse con otras estructuras, como la escena del mantenimiento El proceso posee las características del ahorro de tiempo, conveniente y ampliamente utilizado en metalurgia, carbón, cemento, estación de energía, vidrio, minería, materiales de construcción, ladrillo e industria petroquímica, en comparación con otros materiales, tiene un rendimiento de alto costo, ha sido favorecido por más y más compradores.
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.